BURGUNDY
burgundy clay
Burgundy is an iron bearing, silty clay recommended for low and mid range firing applications. Material Safety Data Sheet
Chemical Anaylis
Al2O3 15.90%
SiO2 58.20%
Na2O 1.40%
K2O 2.10%
CaO 2.09%
MgO 3.11%
TiO2 0.68%
Fe2O3 5.90%
Sieve Analysis
Mesh Size Percent Retained
80 Mesh 0.1%
200 Mesh 8.8%
325 Mesh 22.0%
Color
Dry Brown
Fired red
Loss on Ignition 7.3%
Shrinkage
Dry Cone 05 Cone 1 Cone 5 Cone 10
8% 8.5% 12% 15.3%
Absorption
NA 15.36% 8.2% 9%
SANDY WHITE
sandy white clay
Sandy White is a naturally occuring blend of high quality silica (49%), Kaolin (42%), and feldspar(5%). It is used as a filler in clay bodies to increase both strength and workability. Material Safety Data Sheet
Chemical Anaylis
Al2O3 26.50%
SiO2 64.6%
Na2O 0.05%
K2O 0.30%
CaO 0.13%
MgO 0.14%
TiO2 0.64%
Fe2O3 0.90%
Sieve Analysis
Mesh Size Percent Retained
80 Mesh 0%
200 Mesh 10%
325 Mesh 40%
Color
Dry White
Fired White
Loss on Ignition 4.2%
Shrinkage
Dry Cone 05 Cone 1 Cone 5 Cone 10
1.75% 2% 2% 2% 2%
Absorption
NA 18.1% 12.3% 13.3% 1.6%
M4 CLAY
m4 clay
M4 clay is a light colored plastic fire clay that can be used in a variety of applications. Material Safety Data Sheet
Chemical Anaylis
Al2O3 27.10%
SiO2 54.30%
Na2O 0.07%
K2O 1.01%
CaO 0.03%
MgO 0.54%
TiO2 1.48%
Fe2O3 2.67%
Sieve Analysis
Mesh Size Percent Retained
80 Mesh 0%
200 Mesh 0.3%
325 Mesh 3.6%
Color
Dry Cream
Loss on Ignition 10.8%
Shrinkage
Dry Cone 05 Cone 1 Cone 5 Cone 10
8% 9% 11.5% 13% 16%
Absorption
NA 26.9% 21.7% 18.3% 7.5%
LATERITE
laterite clay
Laterite is a clay with a high iron and alumina content. It is often employed as an inexpensive source of alumina for red clay bodies. Material Safety Data Sheet
Chemical Anaylis
Al2O3 32.50%
SiO2 42.90%
Na2O 0.08%
K2O 0.13%
CaO 0.12%
MgO 0.07%
TiO2 2.06%
Fe2O3 23.80%
Sieve Analysis
Mesh Size Percent Retained
80 Mesh 0%
200 Mesh 7%
325 Mesh 20.7%
Color
Dry Red
Fired Red
Loss on Ignition 10.9%
Shrinkage
Dry Cone 05 Cone 1 Cone 5 Cone 10
6% 8.5% 10.5% 14.5% 15.5%
Absorption
NA 21.87% 19.1% 14.1% 11.1%
IMCO 800
imco 800 fire clay
IMCO 800 is a milled and air floated Lincoln fire clay. It is an excellent all purpose clay with high strength and plasticity. Material Safety Data Sheet
Chemical Anaylis
Al2O3 28.60%
SiO2 53.20%
Na2O 0.15%
K2O 1.69%
CaO 0.18%
MgO 0.67%
TiO2 1.27%
Fe2O3 4.51%
Sieve Analysis
Mesh Size Percent Retained
80 Mesh %
200 Mesh %
325 Mesh %
Loss on Ignition 7.3%
Color
Dry Cream
Cone 05 to 5 Cream
Cone 10 Buff
Loss on Ignition 7.3%
Shrinkage
Dry Cone 05 Cone 1 Cone 5 Cone 10
6% 8.5% 13% 13.5% 15.2%
Absorption
NA 24.3% 14.2% 14.2% 2.2%
IMCO 400
imco 400 fire clay
IMCO 400 is a milled and air floated Lincoln fire clay. It is an excellent all purpose clay with high strength and plasticity. Material Safety Data Sheet
Chemical Anaylis
Al2O3 28.50%
SiO2 52.00%
Na2O 0.14%
K2O 1.42%
CaO 0.66%
MgO 0.66%
TiO2 1.28%
Fe2O3 2.25%
Sieve Analysis
Mesh Size Percent Retained
80 Mesh 0.1%
200 Mesh 0.4%
325 Mesh 1.3%
Color
Dry Cream
Cone 05 to 5 Buff
Cone 10 Buff
Loss on Ignition 7.3%
Shrinkage
Dry Cone 05 Cone 1 Cone 5 Cone 10
7.75% 9.5% 13.5% 13.5% 16.0%
Absorption
NA 21.5% 12.3% 13.3% 1.6%
Edwin
edwin clay
Edwin Clay, previously known as Howard Clay, is a highly plastic fire clay with low free sislica. It is used in many types of ceramic and industrial applications. Material Safety Data Sheet
Chemical Anaylis
Al2O3 29.00%
SiO2 48.50%
Na2O 0.00%
K2O 0.57%
CaO 0.22%
MgO 0.44%
TiO2 1.68%
Fe2O3 2.24%
Sieve Analysis
Mesh Size Percent Retained
80 Mesh 0.1%
200 Mesh 1.8%
325 Mesh 9.7%
Color
Dry Cream
Cone 05 to 5 Buff
Cone 10 Buff
Loss on Ignition 16.0%
Shrinkage
Dry Cone 05 Cone 1 Cone 5 Cone 10
7.75% 8.0% 10.0% 13.0% 15.5%
Absorption
NA 23.8% 21.2% 15.3% 8.4%
C-RED
c-red clay
C-Red is a fine grained, iron bearing, plastic clay. Great for throwing bodies or anybody where warm color and plasticity is desired. Like all our milled clays C-red is air floated. Material Safety Data Sheet
Chemical Anaylis
Al2O3 24.30%
SiO2 49.30%
Na2O 0.05%
K2O 0.38%
CaO 0.30%
MgO 0.26%
TiO2 1.03%
Fe2O3 12.70%
Sieve Analysis
Mesh Size Percent Retained
80 Mesh 0.1%
200 Mesh 4.0%
325 Mesh 12.2%
Color
Dry Red
Cone 05 Orange
Cone 1-10 Red
Loss on Ignition 11.8%
Shrinkage
Dry Cone 05 Cone 1 Cone 5 Cone 10
7.5% 9.0% 11.8% 12.5% 14.0%
Absorption
NA 22.3% 17.3% 17.3% 12.4%
.
Industrial Minerals Company
7268 Frasinetti Road
Sacramento, CA 95828
916-383-2811